Spinner Hanger Hook Machines

The hook type shot blasting machine is the standard model of the shot blasting machine. Its working cylinder diameter is from 900 to 1300mm, and the height is from 1300 to 2200mm.The standard model comes with 2-7 throwing heads and the maximum load capacity is 10,000 kg.

The spinner hanger hook machine has a frame, a shot blasting room, a shot blasting device and a circulating conveying device.

There are more than two shot blasting chambers inside the rotating chamber. The shot blasting chambers are spaced apart on the sides and open outside. The upper part of the hook of the shot blasting chamber communicating with the shot blasting device is connected with the transmission device.

The fixed is matched with the upper part of the rotating chamber body, and a flexible sealing plate is arranged between the side plate of the fixed chamber body and the closing plate of the rotating chamber body.

The sand separation device in the upper part of the shot blasting machine includes a box body, a rolling hole screen, a fixed screen air channel and a discharge plate. The lower part of the discharge plate has a baffle plate, and the waste adjustment plate at the junction of the shot bin and the waste bin is hinged .The cabinet has good cleaning effect and high working efficiency.

The spinner hanger hook machine is suitable for surface treatment and deburring of aluminum parts, rust removal of forgings and sand removal of castings.

　　Automotive Shot Blasting and Peening solutions

　　Sandblasting is to use compressed air to spray abrasive to the surface of workpiece at high speed. The purpose of sandblasting is to improve the appearance quality of workpiece surface by removing oxide layer and rust. Shot peening is to make the high-speed hard particles (generally steel particles) hit the surface of metal workpiece, in order to improve the fatigue strength of metal surface. Sand blasting and shot blasting are two different processes and different tools are used. However, both of them can be recycled.

　　The technology of shot blasting cleaning machine replaces the common cold and hot forming process to form large thin-walled aluminum parts, which can not only avoid the residual tensile stress on the surface of the parts, but also obtain the favorable compressive stress for the parts.

　　It should be noted that the service temperature of the parts treated by shot blasting machine should not be too high, otherwise the compressive stress will disappear automatically at high temperature, thus the expected effect will be lost. Their service temperature is determined by the material of the parts, which is about 260-290 ℃ for general steel parts and 170 ℃ for aluminum parts.